NiCr alloys
162
Crowns and bridges
remanium® G-soft
Proven NiCr alloy for crown and bridge work and
composite veneering.
Advantages:
• reliable melting and casting characteristics
• easy polishing and high lustre
• high corrosion resistance
• high strength for delicate frameworks
• ideal for melting with a flame, as it does not spray
during melting
Indication: crowns and bridges, double crowns,
implant supported supra-structures, Maryland bridges
Norm: DIN EN ISO 22674 (type 4)
Technical data
0.2% Yield strength Rp0.2 400 MPa
Tensile strength Rm 700 MPa
Hardness 210 HV 10
Elongation A5 10 %
Modulus of elasticity E 165 GPa
Density 8.2 g/cm³
Solidus temperature 1210 °C / 2210 °F
Liquidus temperature 1340 °C / 2444 °F
Weight of casting ingot 6 g
REF 100-001-00 1000 g
Composition (percentage by mass)
Ni Cr Mo Si
66.0 26.5 5.0 1.5
Additional elements < 1 %: B, Mn