CoCr alloys
160
Crowns and bridges
remanium® 2001
CoCr bonding alloy. Easy processing properties.
Advantages:
• exceptionally low viscosity
• flexibility in casting: can be melt in a high frequency
induction casting unit, or with propane/oxygen torch
• rapid processing: no oxide firing cycle required
• suitable for laser welding because it is carbon-free
Indication: crowns and bridges, metal ceramics,
double crowns, Maryland bridges
Norm: DIN EN ISO 9693, DIN EN ISO 22674 (type 5)
Technical data
0.2% Yield strength Rp0.2 660 MPa
Tensile strength Rm 850 MPa
Hardness 336 HV 10
Elongation A5 3,5 %
Modulus of elasticity E 195 GPa
Density 8.6 g/cm³
CTE 25–500 °C / 77–932 °F 14.2 x 10-6 K-1
Solidus temperature 1325 °C / 2417 °F
Liquidus temperature 1415 °C / 2579 °F
Weight of casting ingot 6 g
REF 102-600-02 50 g
REF 102-600-01 1000 g
Composition (percentage by mass)
Co Cr Mo W Si
63.0 23.0 7.3 4.3 1.6
Additional elements < 1 %: Mn, N