CAD/CAM materials
Zirconium oxide blanks
ceraMotion® Z HT Shade
ø 98.3 mm
Monochrome, pre-shaded and highly translucent zirconium oxide for all restorations in the anterior and
posterior area, from the single crown to multi-element restorations or implant substructures.
Suitable for all open CAD/CAM systems.
Advantages and indications:
• safety due to high strength
• highly efficient (no preshading required)
• guarantees consistent shade results thanks to preshaded blanks
• reliable reproducibility of classic V-shades
• particularly suitable for monolithic crowns and bridges
• excellent machinability
• translucency 43 % (non-shaded, 1 mm)
• optimum finishing with ceraMotion® One Touch and veneering with ceraMotion® Zr
Recommended sintering temperature: 1530 °C / 2786 °F
Norm: DIN EN ISO 6872
Color REF (14 mm) REF (18 mm) REF (22 mm) REF (25 mm) Quantity
A1 272-111-14 272-111-18 272-111-22 272-111-25 1 piece
A2 272-112-14 272-112-18 272-112-22 272-112-25 1 piece
A3 272-113-14 272-113-18 272-113-22 272-113-25 1 piece
A3,5 272-115-14 272-115-18 272-115-22 272-115-25 1 piece
A4 272-114-14 272-114-18 272-114-22 272-114-25 1 piece
B1 272-121-14 272-121-18 272-121-22 272-121-25 1 piece
B2 272-122-14 272-122-18 272-122-22 272-122-25 1 piece
B3 272-123-14 272-123-18 272-123-22 272-123-25 1 piece
B4 272-124-14 272-124-18 272-124-22 272-124-25 1 piece
C1 272-131-14 272-131-18 272-131-22 272-131-25 1 piece
C2 272-132-14 272-132-18 272-132-22 272-132-25 1 piece
C3 272-133-14 272-133-18 272-133-22 272-133-25 1 piece
C4 272-134-14 272-134-18 272-134-22 272-134-25 1 piece
D2 272-142-14 272-142-18 272-142-22 272-142-25 1 piece
D3 272-143-14 272-143-18 272-143-22 272-143-25 1 piece
D4 272-144-14 272-144-18 272-144-22 272-144-25 1 piece
Technical data
Material ZrO2 3Y-TZP
Bending strength 1100 MPa
Density > 6.08 g/cm³
Radioactivity < 0.02 Bq/g
Solubility < 10 μg/cm2
CTE 10.5 x 10-6 K-1
The values listed were measured on test samples and are typical for
the material. The product properties may, however, deviate from these
values depending on the component design and the forming process.