CoCr alloys
remanium® star MD II milling blank
ø 98.4 mm
Proven CoCr bonding alloy for CAD/CAM milling systems. Optimized casting structure in implant quality.
Advantages:
• proven remanium® star composition
• certified and time-tested base material for all applications in crown and bridge work
• ductility and strength type 3, DIN EN ISO 22674 suitable for machining
• ideal for ceramic veneering using the conventional CTE range
• excellent laser weldability
Indication: for all constructions manufactured using milling technique such as crowns, bridges,
supra-structures, ceramic bonding with suitable ceramics
Norm: DIN EN ISO 9693, DIN EN ISO 22674 (type 3)
Thickness Border REF Quantity
8 mm without 102-750-01 1 piece
10 mm without 102-751-01 1 piece
12 mm 10 mm 102-752-01 1 piece
13.5 mm 10 mm 102-753-01 1 piece
15 mm 10 mm 102-754-01 1 piece
18 mm 10 mm 102-755-01 1 piece
20 mm 10 mm 102-756-01 1 piece
25 mm 10 mm 102-757-01 1 piece
Technical data
0.2% Yield strength Rp0.2 320 MPa
Tensile strength Rm 506 MPa
Hardness 281 HV 10
Elongation A5 5.9 %
Modulus of elasticity E 202 GPa
Density 8.5 g/cm³
CTE 25–500 °C / 77–932 °F 14.1 x 10-6 K-1
Solidus temperature 1320 °C / 2408 °F
Liquidus temperature 1420 °C / 2588 °F
Composition (percentage by mass)
Co Cr W Si
60.5 28.0 9.0 1.5
Additional elements < 1 %: Fe, Mn, N, Nb