Zirconium oxide blanks
Nacera® Pearl white
ø 98.3 mm
White, highly translucent zirconium oxide.
Advantages and indications:
• for multiple indications – from veneers to wide span bridges supported by implants
• highly translucent and extremely stable: flexural strength 1400 MPa, hardness 1300 HV
• natural translucency for aesthetic monolithic restorations
• flexible sintering temperature 1450 °C - 1550 °C / 2642 °F - 2822 °F
• extremely high-precision fitting thanks to Instant Fit Process (I.F.P.)
Also available in semi-translucent (Nacera® Shell white).
Norm: DIN EN ISO 6872
Thickness Color REF Quantity
10 mm White, highly translucent 270-001-10 1 piece
12 mm White, highly translucent 270-001-12 1 piece
14 mm White, highly translucent 270-001-14 1 piece
16 mm White, highly translucent 270-001-16 1 piece
18 mm White, highly translucent 270-001-18 1 piece
20 mm White, highly translucent 270-001-20 1 piece
25 mm White, highly translucent 270-001-25 1 piece
Technical data
Material ZrO2 3Y-TZP
4 point flexural strength 1200 MPa
Radioactivity < 0.02 Bq/g
Solubility < 13 μg/cm2
CTE 10 x 10-6 K-1
The values listed were measured on test samples and are typical for
the material. The product properties may, however, deviate from these
values depending on the component design and the forming process.