Zirconium oxide blanks
130
CAD/CAM materials
ceraMotion® Z Hybrid
ø 98.3 mm
Multi-shaded and multi-layered zirconium oxide made of two different zirconium oxide materials
for all restorations in the anterior and posterior area. Suitable for all open CAD/CAM systems.
Advantages and indications:
• multiple indications due to high strength in the dentine area
• reliable reproducibility for high-level aesthetics
• natural, smooth shade transition from cervical to incisal
• available in the 9 most popular V-shades and 2 bleach shades
• particularly suitable for monolithic restorations
• excellent machinability
• translucency 43 % to 48 % (non-shaded, 1 mm)
• optimum finishing with ceraMotion® One Touch and veneering with ceraMotion® Zr
Recommended sintering temperature: 1480° C / 2696 °F
Norm: DIN EN ISO 6872
Color REF (14 mm) REF (18 mm) REF (22 mm) Quantity
A1 272-411-14 272-411-18 272-411-22 1 piece
A2 272-412-14 272-412-18 272-412-22 1 piece
A3 272-413-14 272-413-18 272-413-22 1 piece
A3,5 272-415-14 272-415-18 272-415-22 1 piece
A4 272-414-14 272-414-18 272-414-22 1 piece
B1 272-421-14 272-421-18 272-421-22 1 piece
B2 272-422-14 272-422-18 272-422-22 1 piece
C2 272-432-14 272-432-18 272-432-22 1 piece
1, bleach 272-300-14 272-300-18 272-300-22 1 piece
2, bleach 272-400-14 272-400-18 272-400-22 1 piece
Technical data
Material ZrO2 3Y-TZP g 4Y-PSZ
Bending strength 1300 MPa g 1020 MPa
Density > 6.04 g/cm³
Radioactivity < 0.02 Bq/g
Solubility < 20 μg/cm2
CTE 10.5 x 10-6 K-1
The values listed were measured on test samples and are typical for
the material. The product properties may, however, deviate from these
values depending on the component design and the forming process.